Preparation and Thermo-Mechanical Characterization of Chitosan Loaded Methylcellulose-Based Biodegradable Films: Effects of Gamma Radiation - RIIP - Réseau International des Instituts Pasteur Accéder directement au contenu
Article Dans Une Revue Journal of Polymers and the Environment Année : 2011

Preparation and Thermo-Mechanical Characterization of Chitosan Loaded Methylcellulose-Based Biodegradable Films: Effects of Gamma Radiation

Résumé

Chitosan (0.1-1%, w/w), dissolved in 2% ace- tic acid solution, was added into 1% methylcellulose (MC)-based formulation containing 0.5% vegetable oil, 0.25% glycerol and 0.025% Tween®80. Films were prepared by casting. Puncture strength (PS), puncture deformation (PD), viscoelasticity coefficient and water vapour perme- ability (WVP) of the films were measured. The PS value of 312 N/mm was observed for MC-based films containing 0.25% chitosan. Values of PD, viscoelasticity coefficient and WVP of these films were 5.0 mm, 44.1%, and 6.0 g mm/m2 day kPa, respectively. The MC-based films containing 0.25% chitosan were also exposed to gamma radiation (0.5-50 kGy). The PS of the treated films decreased significantly from 312 at 0 kGy to 201 N/mm when treated at a dose of 50 kGy. However, WVP values were not affected by increasing irradiation the dose used. The Fourier Transform Infrared spectroscopy supported the molecular interactions due to addition of chitosan in MC- based films. Thermo gravimetric analysis and differential scanning calorimetric experiments showed that thermal properties of the films were significantly improved by chitosan loading. Surface topography of the films was studied by scanning electron microscopy and found rougher due to chitosan addition.
Fichier sous embargo
Fichier sous embargo
Date de visibilité indéterminée
Loading...

Dates et versions

pasteur-01006102 , version 1 (13-06-2014)

Identifiants

Citer

Ruhul A. Khan, Stéphane Salmieri, Dominic Dussault, Nathalie Tufenkji, Jorge Uribe-Calderon, et al.. Preparation and Thermo-Mechanical Characterization of Chitosan Loaded Methylcellulose-Based Biodegradable Films: Effects of Gamma Radiation. Journal of Polymers and the Environment, 2011, 2012 (20), pp.43-52. ⟨10.1007/s10924-011-0336-y⟩. ⟨pasteur-01006102⟩

Collections

RIIP INRS-IAF
28 Consultations
1 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More